Désignation de l'acier |
Composition chimique en% sauf indication contraire |
Aciers ferritiques résistant à la chaleur |
Name |
Number |
C |
Si |
Mn |
P |
S |
Cr |
Al |
Ni |
N |
Autres |
X10CrAlSi7 |
1.4713 |
0.12 |
0.50/1.00 |
1.00 |
0.040 |
0.015 |
6.00/8.00 |
0.50/1.00 |
|
|
|
X10CrAlSi13 |
1.4724 |
0.12 |
0.70/1.40 |
1.00 |
0.040 |
0.015 |
12.00/14.00 |
0.70/1.20 |
- |
- |
- |
X10CrAlSi18 |
1.4742 |
0.12 |
0.70/1.40 |
1.00 |
0.040 |
0.015 |
17.00/19.00 |
0.70/1.20 |
- |
- |
- |
X10CrAlSi25 |
1.4762 |
0.12 |
0.70/1.40 |
1.00 |
0.040 |
0.015 |
23.00/26.00 |
1.20/1.70 |
- |
- |
- |
X18CrN28 |
1.4749 |
0.15/0.20 |
1.00 |
1.00 |
0.040 |
0.015 |
26.00/29.00 |
- |
- |
0.15/0.25 |
- |
X3CrAlTi18-2 |
1.4736 |
0.04 |
1.00 |
1.00 |
0.040 |
0.015 |
17.00/18.00 |
1.70/2.10 |
- |
- |
0.2 + 4(C + N) < Ti <0.80 |
Aciers austénitiques résistant à la chaleur |
X8CrNiTi18-10 |
1.4878 |
0.10 |
1.00 |
2.00 |
0.045 |
0.015 |
17.00/19.00 |
- |
9.00/12.00 |
- |
Ti: 5 x % C < Ti < 0.80 |
X15CrNiSi20-12 |
1.4828 |
0.20 |
1.50/2.50 |
2.00 |
0.045 |
0.015 |
19.00/21.00 |
- |
11.00/13.00 |
0.11 |
- |
X9CrNiSiNCe21-11-2 |
1.4835 |
0.05/0.12 |
1.40/2.50 |
1.00 |
0.045 |
0.015 |
20.00/22.00 |
- |
10.00/12.00 |
0.12/0.20 |
Ce: 0.03/0.08 |
X12CrNi23-13 |
1.4833 |
0.15 |
1.00 |
2.00 |
0.045 |
0.015 |
22.00/24.00 |
- |
12.00/14.00 |
0.11 |
- |
X8CrNi25-21 |
1.4845 |
0.10 |
1.50 |
2.00 |
0.045 |
0.015 |
24.00/26.00 |
- |
19.00/22.00 |
0.11 |
- |
X15CrNiSi25-21 |
1.4841 |
0.20 |
1.50/2.50 |
2.00 |
0.045 |
0.015 |
24.00/26.00 |
- |
19.00/22.00 |
0.11 |
- |
X12NiCrSi35-16 |
1.4864 |
0.15 |
1.00/2.00 |
2.00 |
0.045 |
0.015 |
15.00/17.00 |
- |
33.00/37,00 |
0.11 |
- |
X10NiCrAlTi32-21 |
1.4876 |
0.12 |
1.00 |
2.00 |
0.030 |
0.015 |
19.00/23.00 |
- |
30.00/34.00 |
- |
Al: 0.15/0.60
Ti: 0.15/0.60 |
X6NiCrNbCe32-27 |
1.4877 |
0.04/0.08 |
0.30 |
1.00 |
0.020 |
0.010 |
26.00/28.00 |
- |
31.00/33.00 |
0.11 |
Al: 0.025
Ce: 0.05/0.10
Nb: 0.60/1.00 |
X25CrMnNiN25-9-7 |
1.4872 |
0.20/0.30 |
1.00 |
8.00/10.00 |
0.045 |
0.015 |
24.00/26.00 |
- |
6.00/8.00 |
0.20/0.40 |
- |
X6CrNiSiNCe19-10 |
1.4818 |
0.04/0.08 |
1.00/2.00 |
1.00 |
0.045 |
0.015 |
18.00/20.00 |
- |
9.00/11.00 |
0.12/0.20 |
Ce: 0.03/0.08 |
X6NiCrSiNCe35-25*) |
1.4854 |
0.04/0.08 |
1.20/2.00 |
2.00 |
0.040 |
0.015 |
24.00/26.00 |
- |
34.00/36.00 |
0.12/0.20 |
Ce: 0.03/0.08 |
X10NiCrSi35-19 |
1.4886 |
0.15 |
1.00/2.00 |
2.00 |
0.030 |
0.015 |
17.00/20.00 |
- |
33.00/37.00 |
0.11 |
- |
X10NiCrSiNb35-22 |
1.4887 |
0.15 |
1.00/2.00 |
2.00 |
0.030 |
0.015 |
20.00/23.00 |
- |
33.00/37.00 |
0.11 |
Nb: 1.00/1.50 |
Acier résistant à la chaleur austéno-ferritique |
X15CrNiSi25-4 |
1.4821 |
0.10/0.20 |
0.8/1.50 |
2.00 |
0.040 |
0.015 |
24.50/26.50 |
3.50/5.50 |
0.11 |
- |
- |
Notes : Les éléments non mentionnés dans le tableau ne peuvent pas être ajoutés intentionnellement à l'acier sans l'accord de l'acheteur, sauf pour la finition de la fonte. Toutes les précautions appropriées doivent être prises pour éviter l’ajout de tels éléments à partir de ferraille et d’autres matériaux utilisés dans la production qui pourraient altérer les propriétés mécaniques et l’adéquation de l’acier. *) Nuance d’acier brevetée. |